When the zinc layer is seriously damaged and endangers the iron matrix, the zinc will produce electrochemical protection on the matrix, the standard potential of zinc is -0.76V and the standard potential of iron is -0.44V. When zinc and iron form microbatteries, the zinc will be dissolved as the anode, and the iron will be protected as the cathode. Obviously, the atmospheric corrosion resistance of hot dip galvanizing is better than that of electric galvanizing.
Electrode application range is wide, can realize a variety of materials, a variety of profiles and a variety of joint forms of welding. (1) Welding between low carbon steel, low alloy steel, medium carbon steel, alloy steel and other metal materials or dissimilar metal materials can be achieved. The weld has good comprehensive mechanical properties, and the tensile strength can reach more than 400MPa. ⑵ Can realize the welding of large plate, steel frame, plate – tube, rod – rod, tube – tube and other profiles. ⑶, can realize docking, Angle, lap, T joint and other joint forms of welding. ⑷ mainly suitable for flat welding.(5) it can surfacing the parts of wear failure, so as to obtain the surface surfacing layer with melting depth, smooth surface and excellent performance. ⑹ It can be realized that no bevel 1 ~ 6mm thick metal sheet single-side welding double-side molding.
With other coatings, the opposite is true. Rust builds up immediately and spreads quickly underneath the coating, causing it to peel. The depletion of zinc in the atmosphere is very slow, about 1/17 to 1/18 of the corrosion rate of steel, and is predictable. Its life span far exceeds that of any other coating. The life of the coating depends on the thickness of the coating in a particular environment. And the coating thickness is determined by the thickness of the steel, that is, the thicker the steel is easy to get thicker coating, so the thick steel part of the same steel structure must also get thicker coating, in order to ensure a longer life.
Galvanized wire coating has galvanized, aluminum, nylon or plastic coating. Zinc plating is divided into thin coating after steel wire plating and thick coating after steel wire drawing. The mechanical properties of thick coating are lower than that of smooth steel wire rope, and it is suitable for use in serious corrosive environment. Aluminized wire rope it is more resistant to corrosion, wear resistance, heat resistance than galvanized wire rope, using the method of production after the first plating. The wire rope coated with nylon or plastic is divided into two kinds: coated rope and coated rope.
Environmental factors should be considered when choosing the thickness of galvanized layer. Galvanized wire in galvanized, pay attention to the above problems, can be well galvanized, to ensure the quality of galvanized wire. Galvanized methods are mainly divided into two types, one is hot dip galvanizing method, the other is electric galvanizing method. This paper mainly introduces the method of galvanizing. Electrogalvanizing is an electrolyte used for galvanizing.
Iron products are common metal products in life. Iron products appear everywhere in our life, but there is a big problem in using iron products. Iron products will rust, and when rust occurs, it will affect the use and appearance of iron products. Adding non-metallic coating: clean, dry and coat the surface of iron and steel products with a layer of protective materials, such as oil, mineral grease, rust-proof grease, plastic and lacquer.
First, galvanizing can enhance the corrosion resistance of the product. Zinc has high potential and excellent anodic protection. When the surface of the product is galvanized, zinc will have an electrochemical reaction with oxygen and water in the environment, thereby forming a dense zinc oxide protective film, preventing the metal from further contact with external oxygen, water and other substances, slowing the corrosion rate of the metal. Galvanized products after wire drawing processing, because the surface of the product has a more dense zinc oxide protective film, it can better resist external corrosion and improve the corrosion resistance of the product.
There are many kinds of galvanized solution, which can be divided into cyanide plating solution and cyanide plating solution. Cyanide galvanizing solution has good dispersion and covering ability, coating crystallization is smooth and fine, simple operation, wide application range, has been used in production for a long time. However, because the plating solution contains highly toxic cyanide, the gas escaping in the plating process is harmful to the health of workers, and the waste water must be treated strictly before discharge.
The purchase of blade barbed rope also needs to consider the higher manual installation cost in the later period. Generally, customers only ask the price of blade barbed rope, and sometimes the installation cost is not taken into account in the budget, which is very unreasonable. Because the installation cost is not cheaper than the rope itself, sometimes even the blade rope and column combined. The blade stabbing rope needs a lot of manpower and material resources for installation. In general, the installation cost is also a relatively large expenditure item in the stabbing rope project.