The wire used for wire mesh is made of low carbon steel wire, medium carbon steel wire, high carbon steel wire, stainless steel wire and other materials woven or welded. Production technology: general braid, embossed braid and spot welding type. If the steel wire as the material, after the equipment processing into a network, so called wire mesh.
3cm electric welding net refers to the square hole net of 3cm mesh, galvanized net, impregnated plastic wire mesh, metal mesh, screen. Wide 0.914 m, 1.02 m, 1.2 m, 1.5 m, 1.8 m, length of each volume in 18 to 30 m, welded wire mesh is a wire drawing, wire with advanced welding equipment on the line of welding and become, can be cold zinc, hot dipped galvanized after welding, jinsu anticorrosive processing, also can use the black wire or change wire drawing, galvanized wire, stainless steel wire welding forming, The electric welding mesh is firm, the mesh surface is smooth, is widely used in construction, breeding, isolation, handicraft manufacturing, filtration, mechanical protection, animal fencing and other aspects, according to the demand can be customized electric welding mesh coil, can also be cut into electric welding mesh.
As we all know, even if it is the same kind of steel wire, because of the steel making process, wire drawing process and equipment are not the same, so the quality of steel wire production is not the same. Due to the different mechanical properties of steel wire itself, flattening process and equipment, the width and elongation of steel wire in the flattening process have different effects. Therefore, in the selection of wire diameter, the following three factors should be considered:
The height of the shield should not be less than two meters. The length of the shield should be the width of the journey and the extension 10 meters away. The vertical load of the handrail on the bridge is 1.2KM/m, and the horizontal external load is 2.5KM/m, both of which should be calculated separately. Galvanized hook mesh belongs to a hook mesh, it is the selection of galvanized wire, hot-dip galvanized wire as raw materials, woven through the hook mesh truncated.
Usually according to the general people, the blade barbed rope is the guardrail, widely used in garden apartments, military bases, private residential areas, government machinery where there is a fence, generally used blade barbed rope. The biggest advantage of the blade is that the protective effect is good, and the installation and maintenance is very convenient, strong isolation ability, good resistance effect, etc.
This method is generally the use of hot rolled laminated plate as raw material, the annealed steel plate is first sent to the pickling workshop, with sulfuric acid or hydrochloric acid to remove the surface of the steel sheet oxygen hot galvanizing method. After pickling, the steel plate immediately enters the tank to soak and wait for galvanized, which can prevent the reoxidation of the steel plate. After pickling, water cleaning, squeeze dry, drying, into the zinc pot, the temperature has been maintained at 445-465℃.
Compared with galvanizing, hot-dip galvanizing has lower production cost and less environmental impact than galvanizing. Because the coating obtained is thicker, hot-dip galvanizing has better protective performance than electric galvanizing, so it is an important protective coating for steel parts used in harsh working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, ocean exploration, metal structure, electric power transmission, shipbuilding and other industries.
Hot dip galvanizing is then oiled and chromed. The quality of hot-galvanized sheet produced by this method is significantly improved compared with that by wet galvanizing method. It is only valuable for small-scale production. Continuous galvanizing production line includes a series of pretreatment procedures, such as alkali degreasing, hydrochloric acid pickling, water washing, solvent coating, drying, etc., and the original plate needs to be annealed in cover furnace before entering the galvanizing line.
The height of the shield should not be less than two meters. The length of the shield should be the width of the journey and the extension 10 meters away. The vertical load of the handrail on the bridge is 1.2KM/m, and the horizontal external load is 2.5KM/m, both of which should be calculated separately. Galvanized hook mesh belongs to a hook mesh, it is the selection of galvanized wire, hot-dip galvanized wire as raw materials, woven through the hook mesh truncated.
On the contrary, the denser the ion deposition, the better the quality of zinc layer. Under the condition that the surface zinc layer is dense and bright, the quality of zinc layer per unit area should reach 80g/m2, and the process parameters should be optimized as follows: current density is 16-20A /dm2, mass concentration of zinc sulfate solution is 500g/L, and pH value is 2.5-3.0.
First, galvanizing can enhance the corrosion resistance of the product. Zinc has high potential and excellent anodic protection. When the surface of the product is galvanized, zinc will have an electrochemical reaction with oxygen and water in the environment, thereby forming a dense zinc oxide protective film, preventing the metal from further contact with external oxygen, water and other substances, slowing the corrosion rate of the metal. Galvanized products after wire drawing processing, because the surface of the product has a more dense zinc oxide protective film, it can better resist external corrosion and improve the corrosion resistance of the product.
In the process of composite electroplating galvanized wire, the plating solution must be stirred to obtain the composite coating in which the particles dispersed in the matrix metal. Stirring methods include mechanical stirring, air stirring, ultrasonic stirring, bath circulation, etc. The acid activation solution in the production process can remove the corrosion products and oxide film on the surface of the low carbon steel wire without excessive corrosion on the matrix.