Hot dip galvanizing is dipped in zinc liquid melted by heating, with fast production speed and thick but uneven coating. The market allows a low thickness of 45 microns and a high of more than 300 microns. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Application range of hot dip galvanizing: because the coating is thicker, hot dip galvanizing has better protective performance than electric galvanizing, so it is an important protective coating for iron and steel parts in harsh working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, power transmission, shipbuilding and other industries, in the field of agriculture such as sprinkler irrigation, greenhouse and construction industry such as water and gas transmission, wire casing, scaffolding, Bridges, highway guardrail and other aspects, has been widely used.
There is also a scaly or boride film or oxide. To remove the photosynovium or oxide commonly used methods are: lead grease removal method, acoustic cleaning method, alkali washing or pickling electrolysis grease to oxide method, these methods in the use of gas or steam harmful to human body, pollution, not environmental protection.
Hot dip galvanizing is to remove oil from the workpiece, pickling, dipping, drying after dipping into the dissolved zinc solution for a certain time, can be brought out. Hot dip galvanizing is an effective way to prevent corrosion of metal. It is mainly used for metal structure facilities in various industries. It is to immerse the steel parts after rust removal into the melting zinc liquid at about 500℃, so that the surface of the steel members is attached with zinc layer, so as to play the purpose of anti-corrosion. The galvanized layer is more firm.
Large roll galvanized wire welding net is made of high quality galvanized wire welding net, wire through the current, after mutual melting, strong connection point, and the formation of metal mesh. In the use of galvanized iron wire to find the thickness and soft and hard to the size of flowers, weight and softness corresponding to the degree, too soft florets to use fine wire, and heavy flowers, flowers with thick stems to use thick wire.
Hot dip galvanized hexagonal net is made of low carbon steel wire by mechanized braided welding and then by hot dip zinc treatment. The net color is white and shiny, thick zinc layer, uniform mesh, flat mesh surface, solder joint tension resistance, high corrosion resistance. The surface of the steel wire is usually protected by hot-dip galvanizing, and the thickness of the galvanized protective layer can be made according to the requirements of customers. Hot-dip galvanizing hexagonal net is another kind of twisting mesh corresponding to the galvanizing hexagonal net.
There are many kinds of galvanized solution, which can be divided into cyanide plating solution and cyanide plating solution. Cyanide galvanizing solution has good dispersion and covering ability, coating crystallization is smooth and fine, simple operation, wide application range, has been used in production for a long time. However, because the plating solution contains highly toxic cyanide, the gas escaping in the plating process is harmful to the health of workers, and the waste water must be treated strictly before discharge.
Hot dip galvanizing, also known as hot dip zinc and hot dip galvanizing, is an effective way of metal corrosion prevention, mainly used in various industries of metal structure facilities. It is to immerse the steel parts after rust removal into the molten zinc liquid at about 500℃, so that the surface of the steel member is attached with zinc layer, so as to play the purpose of anticorrosion.