The duration of the protective effect of galvanized layer on large roll galvanized wire is closely related to the coating thickness. Generally speaking, in the dry main gas and indoor use, the thickness of galvanized layer only 6-12μm, and in the environment is more severe conditions, galvanized layer thickness needs 20μm “to be up to 50μm”. Therefore, the influence of environment should be considered when choosing the thickness of galvanized layer.
Now most people want to choose a few when choosing barbed wire material better thorn rope, but the special barbed wire the better, not right, it is important to choose which model is most suited to their own thorn rope,, although is very simple product, but in the use of these products are for specific situation is different, and has a different effect, Maybe now consumers do not have too much concept of blade barbed rope, in fact, such barbed rope products have a higher safety factor. In addition, there are also more and more barbed rope, dazzling reasons, here is an example to illustrate the choice of special barbed rope.
Each coil of steel wire shall consist of one wire. The surface of the rod shall not have cracks, folds, scars, ears, layers or inclusions. However, indentation, pits, bumps, scratches and pockmarks are allowed, and the depth or height shall not be 0.2mm. There should be no corrosion and oxidation skin on the surface of the steel wire, and oxidation color is allowed by heat treatment. The surface of the wire is allowed to have scratches not exceeding half of the allowable deviation range of the diameter, and local defects not exceeding the allowable deviation of the appropriate diameter.
Cyanogen bath has alkaline zincate bath, ammonium bath, sulfate bath and ammonia chloride bath. Cyanide galvanized solution plating ability is good, the coating lubrication, in production has been selected for a long time, steel mesh chromium plating: chromium plating layer has a high hardness, according to the bath composition and process conditions are different, the hardness can be changed in a large scale 400~1200HV.
The service life of the original galvanized iron welding mesh is very limited. Generally, good iron railings can only be used for about 2 years, and then renovated until the service life, which is not only time-consuming but also has safety risks. After the appearance of zinc-steel railings, the service life has been increased to a great extent in the post-processing. Generally, it can be used for at least 20 years. To improve the service life of zinc steel railings, we first have a brief understanding of the product characteristics of railings. Then from the maintenance aspect, it is necessary to maintain. Maintenance method of electric welding mesh:
Black iron wire application in the process, the main is through the hot metal billet rolling into six point five mm wire rod, and then put it in the drawing into a line of different diameter, the plant and then gradually narrow drawing plate aperture, cooling and annealing, plating process, such as making a variety of different specifications of the wire, the wire compared with ordinary black iron wire, will be more softer, Softness is also very uniform, color is also consistent, widely used in the construction industry, mining, chemical industry, welding mesh, welding coat hanger, reprocessing industry and so on.
Domestic iron wire factory has been able to consume wire rope, radial low steel wire, umbrella steel wire, spring steel wire, bicycle saddle spring steel wire and other products. In the 1980s, hot – plated low carbon steel wire, fan net cover steel wire, carbon structure steel wire, bed steel wire and so on were also published. The elongation of wire is increased after annealing. Make the product more soft and increase the scope of application of the wire.
Dip plastic hook net disposal characteristics and downwind, dip plastic is also a common comparison, surface treatment color comparison is single, generally dark green, however, if you want to change into other colors, dip plastic will be more convenient. Because its inner line or inner tube is generally iron line, so, after a period of time, the inner line or inner tube will slowly corrode outward, compared to the outside of the glue fade, hook net will die.