Different from the general zinc barbed rope, high zinc barbed rope surface zinc content is very high can reach the former 6-8 times, so in the service life also has a great advantage, ordinary products three or five years began to corrosion and the latter will take longer to change. Stainless steel barbed rope is in the material aspect of protection, so the durability is also better, these two products are long in the service life, but in the price is high.
In general, the hardness of a metal is often considered to be the resistance of the material to plastic deformation, scratches, wear, or cutting. In the debugging of zinc wire dipping distance, keep the original speed unchanged, according to the time of dipping zinc, the diameter of steel wire, and then estimate the dipping distance. By adjusting the zinc immersion distance, the zinc immersion time of steel wire of various specifications is shortened by 5s on average compared with that before debugging, so that the zinc consumption per ton of steel wire is reduced from 61kg to 59.4kg.
Large roll galvanized wire is processed by low carbon steel wire rod, through drawing molding, pickling rust removal, high temperature annealing, cooling and other processes. Large roll galvanized wire electroplating temperature should be controlled in 30-50℃. Because of the strong corrosivity of chloride ions in bath, quartz glass heater is generally used. Continuous production does not need heating, but need cooling cooling.
Hot plating wire can generate thicker coating, and there are both pure zinc layer and iron zinc alloy layer, so the corrosion resistance is better. The production power of hot dip galvanizing is particularly high, and the duration of the parts in the hot dip galvanizing tank usually does not exceed lmin. Compared with galvanizing, hot-dip galvanizing has lower production cost and less environmental impact than galvanizing. To plate, tape, wire, tube and other profiles plating, automation degree is higher.
3. Zinc layer structure: The structure of zinc layer includes grain size, grain shape and the combination of zinc layer and substrate, etc., which has a certain impact on corrosion resistance. In general, the finer the grain size, the denser the structure, and the better the corrosion resistance.