Therefore, when zinc reaches saturation in the solid melt, the two elements of zinc and iron atoms diffuse with each other, and the zinc atoms diffused into (or infiltrated into) the iron matrix migrate in the lattice of the matrix and gradually form an alloy with iron, while the iron diffused into the molten zinc liquid forms an intermetallic compound FeZn13 with zinc and sinks into the bottom of the hot-dip galvanized pot, that is, zinc slag. When the workpiece is removed from the zinc leaching solution, the surface of the pure zinc layer is formed, which is hexagonal crystal, and its iron content is not more than 0.003%.
The life of the “wire”, is actually “low carbon steel wire”, carbon content in less than 0.2%. The surface is usually coated with zinc plating because it is easy to rust. Under atmospheric conditions, the galvanized layer will not rust before most of the fall off, relatively soft. The life of the “steel wire”, is carbon content in about 0.6% of the “carbon steel wire”, or carbon content in about 0.8% of the “high carbon steel wire”, they have enough hardness and elasticity after appropriate heat treatment, high strength. Uses such as winding ordinary spring and so on.
Large coil galvanized wire in the zinc immersion distance debugging, keep the original speed unchanged, according to t= KD to determine the zinc immersion time (1), where: t is the zinc immersion time is constant, take 4-7D is the diameter of steel wire mm, and then estimate the zinc immersion distance. By adjusting the zinc dip distance, the zinc dip time of steel wire of various specifications can be shortened by 5s on average. In this way, the zinc consumption per ton of steel wire decreases from 61kg to 59.4kg.
Hook mesh wire diameter has thickness, fine wire diameter is generally 0.5mm-2.0mm, thick wire diameter can be in 5mm-22mm. Hook mesh is also customized according to different uses, in general, fine silk can be woven into a relatively small hole, thick silk is generally called heavy hook mesh, mainly used in the screening of stones and coal, in short, hook mesh has an important role in many professions.
We must have a certain understanding of the hexagonal network, we are swayed by the beautiful shape of the hexagonal network, not only the shape of the hexagonal network is very beautiful, in fact, the practical value of survival is very high. The relevant information of Shaojie should be very clear to know that the high speed road guardrail network, hexagonal mesh of all kinds of guardrail network, the value of the high speed road is more prominent, it is not only used in a variety of roads, in a variety of sports ball venues and landslides to take care of, but also to reach a very close utility.
The size of the dog cage is generally relatively small, suitable for indoor small dogs, dog cage is easy to carry, go out to compare the use, folding dog cage high strength steel wire and steel pipe material, the outer layer spray treatment. Strong texture, excellent rust resistance, the dog cage inside the tray, can be pulled out, convenient to clean the dog’s urine and feces, folding, dog cage is suitable for families and pet stores to raise more pet dogs.
Hot dip galvanizing is dipped in zinc liquid melted by heating, with fast production speed and thick but uneven coating. The market allows a low thickness of 45 microns and a high of more than 300 microns. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Application range of hot dip galvanizing: because the coating is thicker, hot dip galvanizing has better protective performance than electric galvanizing, so it is an important protective coating for iron and steel parts in harsh working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, power transmission, shipbuilding and other industries, in the field of agriculture such as sprinkler irrigation, greenhouse and construction industry such as water and gas transmission, wire casing, scaffolding, Bridges, highway guardrail and other aspects, has been widely used.
Hot-dip galvanized wire is widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, electric power transmission, shipbuilding and other industries. It has been widely used in recent years in agricultural fields such as agricultural medicine sprinkler irrigation, greenhouse and construction industry such as water and gas transmission, wire casing, scaffolding, Bridges, highway guardrail and so on.
Environmental factors should be considered when choosing the thickness of galvanized layer. Galvanized wire in galvanized, pay attention to the above problems, can be well galvanized, to ensure the quality of galvanized wire. Galvanized methods are mainly divided into two types, one is hot dip galvanizing method, the other is electric galvanizing method. This paper mainly introduces the method of galvanizing. Electrogalvanizing is an electrolyte used for galvanizing.
Different from common zinc barbed rope, high zinc barbed rope surface zinc content is very high can reach 6-8 times of the former, so there is a great advantage in the service life, ordinary products begin to corrosion three to five years while the latter will take longer to change. Stainless steel barbed rope is in material protection so durability is also better, these two products are long service life, but in terms of high price.
For the wide use of screen, the state has regulations. You also specify the diameter size, mesh size, or usage method. For plastering mesh, mesh should be less than 20 and diameter greater than 1 nm. Not only are specifications specified, but safety is preferred if wire mesh is used in exterior plastering mesh. If you fall, the consequences are unimaginable. Therefore, the application of norms should be combined with reality.
Stainless steel wire is characterized by good corrosion, in chemical plants or pharmaceutical industry can often be used to stainless steel wire, suitable for acid, alkali environment. Aluminum alloy wire is characterized by high temperature, can adhere to the high temperature of more than 100 degrees Celsius does not fade, and has good corrosion, patience is also very good. It can be used for device manufacturing in construction industry.
Some customers may not use the blade rope immediately when they buy it, some are retail, and some are temporarily not used in site construction. At this time, it is necessary for customers to follow up the characteristics of the blade rope for storage. Because they are afraid of rain, so this is needless to say, and the surface of the packaging is more afraid of the sun, so it is not recommended to prevent outdoor exposure to sunlight will cause the woven bag to become ineffective, resulting in the internal blade of the rope exposed to affect the later use.