Galvanized wire is processed by low carbon steel wire rod. It is made of low carbon steel, after drawing forming, pickling and rust removal, high temperature annealing, hot dip galvanizing, cooling and other processes. Electrogalvanized iron wire using low carbon steel as raw materials, after drawing, galvanized and other processes completed. It has the characteristics of galvanized layer, strong corrosion resistance, strong galvanized layer, and so on. Galvanized iron wire is widely used in construction, highway walls, Zahua, weaving and other industries.
The quality of hot-dip galvanized barbed wire is only good in the surface of the wire attached to the galvanized layer, and with the chemical reaction, the surface of the zinc layer will gradually lose effect because of the oxidation reaction, this situation is more prominent in the humid area of the environment. And because after all, it is rusty iron wire, so the quality of hot-dip galvanized barbed rope is certainly not up to the level of stainless steel barbed rope.
Cold galvanizing is in the plating tank through the current unidirectional zinc gradually plated on the metal appearance, the production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, smooth, high aesthetics, poor corrosion resistance, generally a few months will rust. Hot dip galvanized coating is thicker, generally 30-60 microns, coating corrosion resistance is higher. Suitable for outdoor work of steel parts, such as highway fences, power towers, large size fasteners and other more “rough” workpiece long-term rust prevention.
Hot dip galvanizing is dipped in zinc liquid melted by heating, with fast production speed and thick but uneven coating. The market allows a low thickness of 45 microns and a high of more than 300 microns. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Application range of hot dip galvanizing: because the coating is thicker, hot dip galvanizing has better protective performance than electric galvanizing, so it is an important protective coating for iron and steel parts in harsh working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, power transmission, shipbuilding and other industries, in the field of agriculture such as sprinkler irrigation, greenhouse and construction industry such as water and gas transmission, wire casing, scaffolding, Bridges, highway guardrail and other aspects, has been widely used.
Our country industry chooses the low carbon steel with good quality as raw material, and then produces the quality galvanized iron wire by drawing, galvanizing and other processes. Now the production technology of galvanized iron wire products can be divided into hot plating and electroplating two kinds of methods. No matter which one is chosen, it should be carried out in accordance with the corresponding operating specifications, so as to better ensure the production of good products. For key and important parts with tensile strength greater than 1034mpa before plating, the stress should be released at 200±10℃ for more than 1 hour and 140±10℃ before plating.