Galvanized wire coating rough, passivation film is not bright, bath temperature is too high. If the cathode current density is too high, zinc content in the bath is too high or sodium hydroxide and DPE content is too low; Solid particles or excessive foreign metal impurities in the electroplating solution can cause such problems. Solution: If the coating of large galvanized wire is rough, there may be solid particles in the plating solution. If the roughness of the part is severe, the current density may be too high.
Hot dip galvanizing, also known as hot dip zinc, is the method of forming a layer of zinc coating on the surface of the workpiece after oil removal and rust removal, showing a clean and infiltrating surface, immediately immersed in the plating tank of zinc melting in advance. Cold galvanizing is the same after the removal of oil, in addition to lure, showing no pollution, infiltration of the workpiece hung into a special electroplating tank on the cathode, the anode with zinc. Switch on the DC power supply, zinc ions on the anode migrate to the cathode, and discharge on the cathode, so that the workpiece is coated with a layer of zinc layer hot dip galvanizing method.
Hot wire is made of high quality low carbon steel, high carbon steel, after drawing, hot galvanized processing galvanized wire. Hot dip galvanized wire production process: wire rod – drawing – annealing – drawing – annealing – galvanized. Hot dip galvanized wire has the characteristics of thick coating, strong corrosion resistance and solid coating. And according to the special needs of users, according to the industry standard to provide various specifications of galvanized wire. Hot-dip galvanized wire is of better quality than electrodip galvanized wire. In the production process, hot dip galvanized wire has more than one annealing process, so the corrosion resistance of hot dip galvanized wire is stronger than that of electric galvanized wire.
Galvanized wire coating is galvanized, aluminum plated, coated with nylon or plastic, etc. Zinc is divided into thin coating of steel wire after plating and thick coating of galvanized steel wire after drawing. The mechanical properties of thick coating are reduced compared with smooth steel wire rope, which should be used in severe corrosion environment. It is more resistant to corrosion, wear and heat than galvanized wire rope, using the first plating and then drawing method of production. Coated nylon or plastic wire rope is divided into two kinds of coated rope and coated stock after the rope.