“Dry” hot dip galvanizing is also called “drying solvent method” hot dip galvanizing. Iron and steel work pieces through degreasing, pickling, cleaning, dipping aid solvent and drying, and then immersed in the molten zinc solution to galvanize. The co-solvent is usually hydrochloric acid, ammonium chloride, or ammonium chloride mixed with zinc chloride in aqueous solution.
Hot-dip galvanized wire is widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, electric power transmission, shipbuilding and other industries. It has been widely used in recent years in agricultural fields such as agricultural medicine sprinkler irrigation, greenhouse and construction industry such as water and gas transmission, wire casing, scaffolding, Bridges, highway guardrail and so on.
Domestic iron wire factory has been able to consume wire rope, radial low steel wire, umbrella steel wire, spring steel wire, bicycle saddle spring steel wire and other products. In the 1980s, hot – plated low carbon steel wire, fan net cover steel wire, carbon structure steel wire, bed steel wire and so on were also published. The elongation of wire is increased after annealing. Make the product more soft and increase the scope of application of the wire.
If the zinc coating is good, but when the light comes out in 3% nitric acid, there is a dark shadow on the coating, and the film is brown when passivation occurs, which may be caused by foreign metal impurities such as copper or lead in the galvanized liquid. When there is a problem in the process of galvanizing, check the temperature and current density first, and then measure and adjust the content of zinc and sodium hydroxide in the bath through the analysis of the bath. Whether DPE levels are low can be determined by Hull cell test.
Hot dip galvanizing is dipped in zinc liquid melted by heating, with fast production speed and thick but uneven coating. The market allows a low thickness of 45 microns and a high of more than 300 microns. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Application range of hot dip galvanizing: because the coating is thicker, hot dip galvanizing has better protective performance than electric galvanizing, so it is an important protective coating for iron and steel parts in harsh working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, power transmission, shipbuilding and other industries, in the field of agriculture such as sprinkler irrigation, greenhouse and construction industry such as water and gas transmission, wire casing, scaffolding, Bridges, highway guardrail and other aspects, has been widely used.
Dog cage mainly by welding, spraying, injection molding, surface treatment, electroplating dog cage is made of high quality steel wire, dog cages are with plastic and plastic surface treatment, electrophoresis, chrome plating, galvanized, imitation gold, etc., according to the customer request processing, respectively, also can be customized to sample, dog cage assembly of compact structure, neat and beautiful appearance, make folding and remove the cage is more convenient and quick, won’t take up too much space.